Hastelloy Alloy C-4

Hastelloy Alloy C-4
Product Details

Hastelloy C-4 (UNS No6455)


Chemical Composition
Wt.%

%

Ni

Cr

Fe

C

Mn

Si

Mo

Al

Ti

P

S

min

bal

14.5





14





max

bal

17.5

3.0

0.015

1

0.08

17

0.3

0.70

0.02

0.03

Physical
Constants

Density.g/cm³

8.6 g/cm³

Melting Range

1335-1380 ℃

The minimum mechanical properties of the alloy at room temperature

Typical mechanical properties

tensile strength
Rm N/mm2

Yield Strength
RP0.2N/mm2

Elongation
A5 %

HB

Solution treatment

690

276

40

≤200

Microstr ycture

The alloy is face-centered cubic lattice structure, its chemical composition to ensure the stability of the metallographic and anti-sensitization.

Characters

Resistance to chloride ion oxidation - reduction composite corrosion, tissue thermal stability

Process

performance

1, In the heat treatment process can not contact with sulfur, phosphorus, lead and other low melting point metal, or alloy will become brittle, should pay attention to remove such as marking paint, temperature indicator paint, colored crayons, lubricants, fuel and other dirt. The lower the sulfur content of the fuel the better, the sulfur content of natural gas should be less than 0.1%, the sulfur content of heavy oil should be less than 0.5%. Electric furnace heating is a better choice, because the electric furnace can accurately control the temperature and the furnace gas is clean. If the gas stove gas pure enough, you can choose.
2, alloy thermal processing temperature range of 1080 ℃ ~ 900 ℃, cooling method for water cooling or other rapid cooling. To ensure the best corrosion resistance, heat treatment should be carried out after solution heat treatment.

Applications

The alloy is an austenitic low-carbon nickel-molybdenum-chromium alloy. The main difference between Nicrofer 6616 hMo and other alloys of similar chemical composition developed earlier is low carbon, silicon, iron and tungsten. This chemical composition provides excellent stability at 650-1040 ℃ and improved resistance to intergranular corrosion, avoiding edge line corrosion susceptibility and weld HAZ corrosion under appropriate manufacturing conditions. Alloy used in flue gas desulfurization systems, pickling and acid regeneration plant, acetic acid and agricultural chemicals production, titanium dioxide production (chloride method), electrolytic plating.

Hot Tags: hastelloy alloy C-4, suppliers, manufacturers, customized, discount, price
Related Products
Quick Navigation
  • About Us
  • Product
  • News
  • Knowledge
  • Contact Us
  • Feedback
  • Newsletter
    Enter in your email address to receive deals and coupons.
    +86-18006107688
    +86-511-86456007 info@hltegang.com